Unigic Nanocomposite Nylon 6 Material "NANOCON®"is a resin material reinforced with a nano-scale (nm) size layered silicate. Different from the common use of micron-level (μm) glass fiber or inorganic mineral reinforcement materials, it is a unique composite material.

Classification:

Key words:

Nano nylon

Special Amine Special Nylon Propanic Acid Monomer Color Separator Kubota Unigico

File Download:

Product Consulting:

Product Description

NANOCON®The characteristics

1. Lightweight, strength, rigidity, high heat resistance... The reinforcement efficiency of the reinforced material is very high.

2. Small changes in size and physical properties due to water absorption... Excellent environmental characteristics

3. The appearance of outstanding color... Layered silicates have a high degree of whiteness

4. Easy to form... Less burr, high speed forming

5. Recyclable... During secondary use, the reinforcing material will not be destroyed.

6. Certain barrier properties... Nanoscale layered silicates are able to block the passage of small molecules through

	ISO test method	Unit	NANOCON ® M1030DH	PA6＋GF15	PA6 + Mineral 35%	PA6
Density	1183	g/cm³	1.15	1.23	1.40	1.13
Water absorption (23 ℃× 50% RH equilibrium)	62	%	2.8	2.4	1.8	2.8
Tensile strength	ISO527	MPa	95	120	70	80
Tensile elongation		%	3	3	3	45
Tensile elasticity rate		MPa	4300	5500	6400	2600
bending strength	178	MPa	155	170	120	100
bending elasticity rate		MPa	4500	5000	6300	2500
Charpy impact strength (notch with/without)	179-1eA	kJ/m2	4 / 57	7 / 23	3 / 41	4 / NB
Thermal deformation temperature (1.8/0.45MPa)	75-1, -2	℃	140 /190	190 / 215	130 / 200	60/ 165
Linear expansion coefficient (flow direction)	11359-2	10-5/℃	5.3	4.2	5.0	9.6
Forming shrinkage 3.2mmt (flow direction/right angle)	Self-Society Law	%	1.1/1.2	0.3-0.5 / 0.8-1.0	0.4 / 0.8	1.5/ 1.6